5154 Aluminum Pipe & Tube Specifications
Standards: ASTM, ASME, AMS, GB/T, JIS
Thickness: 0.2-500mm, etc.
Width: 20-2650mm, etc.
Length: Customized
Shape: Round, Square, Rectangular, etc.
Material Temper: F, O, T4, T6, T651, H14, H112
Delivery Time: 7-20 days.
5154 Aluminum Tube & Pipe Data Sheet
Equivalent Grades Of 5154 Aluminum Tube
Chemical Composition of 5154 Aluminum Tube
Mechanical Properties of 5154 Aluminium Tubes with Different Tempers
| Temper | Tensile Strength (MPa) | Yield Strength (MPa) | Elongation (%) | Hardness (HB) |
|---|---|---|---|---|
| 5154 O (Annealed) | 120 – 175 | 45 – 75 | 30 – 50 | 40 – 60 |
| 5154-H12 (Work Hardened) | 185 – 235 | 105 – 145 | 20 – 30 | 60 – 75 |
| 5154-H22 (Work Hardened & Partially Annealed) | 185 – 235 | 105 – 145 | 20 – 30 | 60 – 75 |
| 5154-H32 (Work Hardened & Solution Heat Treated) | 200 – 250 | 140 – 180 | 15 – 25 | 70 – 85 |
For high-quality 5154 aluminum sheets and professional assistance, contact HXM, your reliable supplier of aluminum products.
Physical Properties of 5154 Aluminum Tube Metal
| Property | Value | Units |
|---|---|---|
| Density | 2.68 – 2.72 | g/cm³ |
| Melting Point | 605 – 650 | °C |
| Thermal Conductivity | 120 – 140 | W/m·K |
| Electrical Conductivity | 30 – 40 | % IACS* |
| Specific Heat Capacity | 0.897 | J/g·K |
| Modulus of Elasticity | 69 – 71 | GPa |
| Poisson’s Ratio | 0.33 | – |
| Thermal Expansion Coefficient | 22.7 x 10^-6 | /°C |
| Surface Finish | Smooth, can be anodized or coated | – |
Different Tempers of 5154 Aluminum Tubes Metal
O (Annealed): This temper involves heating the aluminum to a high temperature and then slowly cooling it to relieve internal stresses and soften the material. It is suitable for applications requiring high formability and ease of machining.
H12 (Work Hardened): This temper is achieved by cold working the aluminum, which increases its strength and hardness. It is commonly used in applications where moderate strength and good workability are needed.
H22 (Work Hardened & Partially Annealed): This temper combines work hardening with partial annealing. The partial annealing reduces some of the hardness and brittleness, offering a balance between strength and ductility.
H32 (Work Hardened & Solution Heat Treated): This temper involves solution heat treatment followed by work hardening. It provides higher strength and improved mechanical properties compared to the O and H12 tempers while retaining good ductility.
Applications of 5154 Aluminum Pipe Metal
5154 Aluminum Pipe & Tube Packages
The following is our company’s standard aluminum pipe & tube export packaging. If the customer has any packaging requirements, our company can meet them.