2014 Aluminum Pipe & Tube Specifications
Standards: ASTM, ASME, AMS, GB/T, JIS
Thickness: 0.2-500mm, etc.
Width: 20-2650mm, etc.
Length: Customized
Shape: Round, Square, Rectangular, etc.
Material Temper: F, O, T4, T6, T651, H14, H112
Delivery Time: 7-20 days.
2014 Aluminum Tube & Pipe Data Sheet
Equivalent Specifications of Aluminum 2014 Tube
Here is a table displaying the equivalent specifications of the Aluminum 2014 tube:
| Standard Organization | Specification/Standard | Description |
|---|---|---|
| ASTM | ASTM B210 | Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes |
| AMS | AMS 4085 | Aluminum Alloy Tubing, Seamless, Drawn, 4.4Cu – 0.8Si – 0.8Mn – 0.5Mg – 0.5Zn – 0.1Cr, 2014-T6 |
| AMS | AMS 4087 | Aluminum Alloy Tubing, Seamless, Drawn, 4.4Cu – 0.8Si – 0.8Mn – 0.5Mg – 0.5Zn – 0.1Cr, 2014-T4510 |
| UNS | UNS A92014 | Unified Numbering System designation for 2014 alloy |
| ISO | ISO 6362-2 | Wrought aluminum and aluminum alloys — Extruded rods/bars, tubes, and profiles — Part 2: Mechanical properties |
| BS | BS EN 754-2 | Aluminum and aluminum alloys – Cold drawn rod/bar and tube – Part 2: Mechanical properties |
| BS | BS EN 754-8 | Aluminum and aluminum alloys – Cold drawn rod/bar and tube – Part 8: Porthole tubes, tolerances on dimensions and form |
| DIN | DIN 3.1255 | Aluminum alloy, technical specifications for wrought products |
| AA | AA 2014 | Aluminum Association designation |
| Europe | AlCu4SiMg | European equivalent designation |
This table shows the various standards and specifications equivalent to Aluminum 2014 pipes. If you want to know more news, you can contact us directly!
Chemical Composition of 2014 Aluminum Pipes
| Element | Al | Cu | Mg | Mn | Si | Fe | Zn | Ti | Others |
|---|---|---|---|---|---|---|---|---|---|
| Percentage (%) | 90.7 – 94.7 | 3.9 – 5.0 | 0.2 – 0.8 | 0.4 – 1.2 | 0.5 – 1.2 | 0.7 max | 0.25 max | 0.15 max | 0.15 max each, 0.05 max total |
There are some differences in the chemical composition of aluminum products from different aluminum manufacturers, but they are all within a certain range. If you want to know more, please contact us directly!
Mechanical Properties of 2014 Aluminium Tubes
Here is a table summarizing the mechanical properties of 2014 aluminum tubes under different temper conditions:
| Property | O (Annealed) | T3 | T4 | T6 | T6510 |
|---|---|---|---|---|---|
| Tensile Strength (MPa) | 210 – 270 | 380 – 460 | 400 – 480 | 450 – 505 | 470 – 530 |
| Yield Strength (MPa) | 110 – 200 | 240 – 320 | 250 – 350 | 385 – 450 | 410 – 470 |
| Elongation (% in 50mm) | 18 – 20 | 10 – 15 | 12 – 18 | 10 – 12 | 9 – 11 |
| Hardness (HB) | 60 – 75 | 105 – 120 | 110 – 125 | 120 – 140 | 125 – 145 |
Physical Properties of 2014 Aluminum Tubes
| Property | Value |
|---|---|
| Density | 2.80 g/cm³ |
| Melting Point | 510 – 638 °C (950 – 1180 °F) |
| Thermal Conductivity | 160 W/m·K |
| Electrical Conductivity | 36% IACS (International Annealed Copper Standard) |
| Coefficient of Thermal Expansion | 23.2 µm/m·K (20-100°C) |
| Modulus of Elasticity | 73.1 GPa |
| Poisson’s Ratio | 0.33 |
Tempers of 2014 Aluminum Pipes
O Temper (Annealed):
- The material is fully annealed for maximum ductility and lowest strength.
- Ideal for forming and bending applications.
T3 Temper:
- After solution heat treatment, the material is cold-worked.
- Offers a balance of moderate strength and good ductility.
T4 Temper:
- The material undergoes solution heat treatment and natural aging.
- Results in higher strength while maintaining good ductility.
T6 Temper:
- The material is solution heat-treated and artificially aged.
- Provides high strength with reduced ductility, suitable for high-stress applications.
T651 Temper:
- Similar to T6 but includes stress relief by stretching.
- Offers high strength and good dimensional stability.
T6510 Temper:
- Similar to T651 but includes additional straightening.
- Ensures straightness and precision for specific applications.
T6511 Temper:
- Includes adjustments for different types of products while maintaining high strength.
- Ensures straightness for precision applications.
H Temper (Strain-hardened):
- Achieves increased strength through cold working.
- Less common for 2014 aluminum as this alloy is mainly heat-treatable.
For more information or pricing on 2014 aluminum tubes, please get in touch with HXM and our team will respond to your message within 24 hours!
Applications of 2014 Aluminum Pipe Metal
Aerospace Components: such as fuselage frames and wing ribs, require high strength and good wear resistance.
Military Equipment: Suitable for manufacturing parts such as armor plates and structural components that require high strength and toughness.
Automotive Parts: Such as suspension components and engine parts require high performance and reliability.
Engineering Applications: Used in various engineering and industrial applications that require high strength and good machinability.
2014 Aluminum Pipe & Tube Packages
The following is our company’s standard aluminum pipe & tube export packaging. If the customer has any packaging requirements, our company can meet them.