2011 Aluminum Wires

2011 Aluminum Wire Specifications

Diameter: 0.5mm-15mm

Length: Roll

Alloy Temper: HO,H12,H14,H16,H18,H19,H22,H24,H26,H28,F,H112,T651,T3,T451, T4,T6, ect.

Craft: Cutting, hemming, arc bending, welding, grinding, spraying, forming

Surface: Mill finish, no stains, without rough selvage, Anodizing

Certificate: ISO9001, CE, SGS, etc

Delivery Time: 7-20 days.

2011 Aluminum Wire Data Sheet

Equivalent Specifications of Aluminium 2011 Wires

here’s a table displaying the equivalent specifications of the Aluminum 2011 Wires

Specification	Standard/Organization	Details
EN	EN AW-2011	European Norm equivalent for 2011 aluminum alloy
ASTM	ASTM B209	Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
UNS	UNS A92011	Unified Numbering System designation for 2011 aluminum
AA	AA2011	Aluminum Association designation for 2011 alloy
ISO	ISO 6361	International Organization for Standardization – Wrought aluminum and aluminum alloy sheets, strips, and plates
DIN	DIN 3.1655	Deutsches Institut für Normung (German Institute for Standardization) equivalent for 2011 aluminum
JIS	JIS H 4000	Japanese Industrial Standards for aluminum and aluminum alloys
GB	GB/T 3190	National Standard of the People’s Republic of China for aluminum and aluminum alloy chemical composition
AMS	AMS 4027	Aerospace Material Specification for 2011 aluminum alloy sheets and plates
SAE	SAE J454	Society of Automotive Engineers – Wrought aluminum and aluminum alloy sheets and plates

This table outlines the various standards and specifications that are equivalent to Aluminum 2011 Wires. If you would like more information, please contact us directly!

Chemical Composition of 2011 Aluminum Wires

Here is the chemical composition of the 2011 Aluminum Wires:

Element	Composition (%)
Al	Balance
Cu	5.0 – 6.0
Fe	≤ 0.7
Si	≤ 0.4
Zn	≤ 0.3
Pb	0.2 – 0.6
Bi	0.2 – 0.6
Others	Each ≤ 0.05%, Total ≤ 0.15

This is the specific percentage range of various elements of the 2011 aluminum wires, which ensures its unique properties and performance characteristics. If you want to know more, please contact us directly!

Mechanical Properties of 2011 Aluminium Wires

Property	Value
Ultimate Tensile Strength	310 MPa (45 ksi)
Yield Strength	276 MPa (40 ksi)
Elongation	Approximately 10% in 2 inches
Hardness	95 HB
Modulus of Elasticity	69 GPa (10,000 ksi)
Shear Strength	207 MPa (30 ksi)

The mechanical properties demonstrated above make the 2011 aluminum wires an excellent choice for applications that require high strength and precision machining. Its excellent machinability and ability to achieve a high-quality surface finish ensure its optimal performance in a variety of industrial uses.

For more information on the 2011 aluminum wires or to request a quote, please contact HXM. Our sales team will respond to you within 24 hours!

Physical Properties of 2011 Aluminum Wires

Property	Value
Density	2.85 g/cm³ (0.103 lb/in³)
Melting Point	502 – 638°C (936 – 1180°F)
Thermal Conductivity	121 W/m·K
Electrical Conductivity	32% IACS
Coefficient of Thermal Expansion	23.6 x 10⁻⁶ /°C (13.1 x 10⁻⁶ /°F)
Specific Heat Capacity	0.87 J/g-°C

These physical properties highlight the excellent thermal and electrical conductivity of the 2011 aluminum wires, as well as its suitability for high-temperature applications due to its melting point range and thermal expansion coefficient. Specific heat capacity and density further highlight the efficiency and reliability of this material.

For more details on 2011 aluminum wires, please contact HXM, our team will respond to you within 24 hours!

Tempers of 2011 Aluminum Wires

Temper Designation	Description	Typical Applications
2011-T3	Solution heat-treated, cold-worked, and naturally aged.	Suitable for applications requiring high strength and good machinability.
2011-T4	Solution heat-treated and naturally aged.	General-purpose applications with a good balance of strength and ductility.
2011-T6	Solution heat-treated and artificially aged.	Offers the highest strength and is used in critical components where high performance is required.
2011-T8	Solution heat-treated, cold-worked, and artificially aged.	Provides excellent machinability and good strength, often used in complex, precision machined parts.
2011-O	Annealed (softened).	Ideal for applications requiring maximum ductility and formability.

These tempering treatments allow 2011 aluminum wires to be customized to specific application requirements, ensuring optimal performance in a variety of industrial and engineering environments.

For more information or pricing on 2011 aluminum wires, please contact HXM and our team will respond to your message within 24 hours!