5056 Aluminum Wires

5056 Aluminum WireSpecifications

Diameter: 0.5mm-15mm

Length: Roll

Alloy Temper: HO,H12,H14,H16,H18,H19,H22,H24,H26,H28,F,H112,T651,T3,T451, T4,T6, ect.

Craft: Cutting, hemming, arc bending, welding, grinding, spraying, forming

Surface: Mill finish, no stains, without rough selvage, Anodizing

Certificate: ISO9001, CE, SGS, etc

Delivery Time: 7-20 days.

5056 Aluminum Wire Data Sheet

Chemical Composition of 5056 Aluminum Wire

Element	Range (%)
Al	Balance
Mg	4.5 – 5.5
Cr	0.05 – 0.20
Fe	≤ 0.7
Cu	≤ 0.10
Mn	≤ 0.10
Si	≤ 0.30
Zn	≤ 0.10
Others (each)	≤ 0.05
Others (total)	≤ 0.15

There are some differences in the chemical composition of aluminum products from different aluminum manufacturers, but they are all within a certain range. If you want to know more, please contact us directly!

Mechanical Properties of 5056 Aluminum Wire

Property	Temper O	Temper H12	Temper H14	Temper H16	Temper H18
Tensile Strength	310 MPa (45 ksi)	345 MPa (50 ksi)	379 MPa (55 ksi)	414 MPa (60 ksi)	450 MPa (65 ksi)
Yield Strength	275 MPa (40 ksi)	310 MPa (45 ksi)	345 MPa (50 ksi)	379 MPa (55 ksi)	414 MPa (60 ksi)
Elongation	12%	10%	8%	7%	6%
Brinell Hardness	90	100	110	115	120

Choose us for reliable 5056 Aluminum Wire solutions that meet your specific needs with precision and quality.

Physical Properties of 5056 Aluminum Wire

Property	Temper O	Temper H12	Temper H14	Temper H16	Temper H18
Density	2.65 g/cm³	2.65 g/cm³	2.65 g/cm³	2.65 g/cm³	2.65 g/cm³
Melting Point	610°C – 650°C	610°C – 650°C	610°C – 650°C	610°C – 650°C	610°C – 650°C
Thermal Conductivity	122 W/m·K	122 W/m·K	122 W/m·K	122 W/m·K	122 W/m·K
Electrical Conductivity	30% IACS	30% IACS	30% IACS	30% IACS	30% IACS
Modulus of Elasticity	70 GPa	70 GPa	70 GPa	70 GPa	70 GPa
Coefficient of Thermal Expansion	22.8 µm/m·°C	22.8 µm/m·°C	22.8 µm/m·°C	22.8 µm/m·°C	22.8 µm/m·°C